Metallurgical effect on the mechanical behavior of rotary endodontic files using finite element analysis

Abstract

Under bending conditions, the maximum Von Misses stress value was related to NiTi file model (330 MPa), followed by M-wire (311 MPa), then CM file model (191 MPa), while the least amount of stress value was related to R-phase file model (169 MPa). When torsion test was performed the maximum stress value was also related to NiTi file model (270 MPa), followed by M-wire (261 MPa), then CM file model (191 MPa), while the least amount of stress value was related to R-phase file model (188 MPa).