Nhan đề : | Applicability of carbothermic reduction for upgrading Sri Lankan ilmenite ores: towards converting ilmenite into synthetic rutile by mechanical activation |
Tác giả: | Wijewardhana, T. Dilmi. U. |
Người tham gia: | Ratnayake, Amila Sandaruwan |
Năm xuất bản : | 2021 |
Số tùng thư/báo cáo: | Bulletin of the National Research Centre, Volume 45 (2021), Article number: 149 |
Tóm tắt : | The milled samples were subsequently heated for two hours continuously at temperatures of 800 °C, 900 °C, 1000 °C, 1100 °C, and 1200 °C, respectively. Initial and annealed samples were analysed using X-ray diffraction (XRD), Fourier-transform infrared (FTIR) spectroscopy, and X-ray fluorescence (XRF) analyses. XRD pattern of the initial sample was characterized by less percentage of rutile (TiO2) peaks and low crystallinity. However, the number of rutile peaks and crystallinity were increased with respective milling hours and annealed temperature. Besides, XRD analysis indicates a higher number of sharp and intense rutile and elemental iron peaks in the samples annealed above 1000 °C. FTIR analysis of raw ilmenite indicates mainly stretching vibrations of Fe–O. However, vibrational spectral bands around 700 cm−1 in samples annealed above 1000 °C are assigned to Ti–O–Ti stretching vibrations. High TiO2 and TiO2 + Fe2O3 (total) wt. (%) can also be observed in samples annealed above 1000 °C. |
URI: | http://tailieuso.tlu.edu.vn/handle/DHTL/12542 |
Nguồn trực tuyến: | https://link.springer.com/article/10.1186/s42269-021-00608-9 |
ISSN : | 2522-8307 |
Trong bộ sưu tập: | Tài liệu mở |
XEM MÔ TẢ
6
XEM & TẢI
0
Danh sách tệp tin đính kèm:
Hiện tại không có tệp tin đính kèm tới tài liệu.
Bạn đọc là cán bộ, giáo viên, sinh viên của Trường Đại học Thuỷ Lợi cần đăng nhập để Xem trực tuyến/Tải về
Khi sử dụng tài liệu trong thư viện số bạn đọc phải tuân thủ đầy đủ luật bản quyền.